Some aspects of barreling in sintered plain carbon steel powder metallurgy preforms during cold upsetting

Narayan, Sumesh and Ananthanarayanan, Rajeshkannan (2012) Some aspects of barreling in sintered plain carbon steel powder metallurgy preforms during cold upsetting. Materials Research, 15 (2). pp. 291-299. ISSN 1516-1439

PDF - Published Version Available under License Creative Commons Attribution. Download (763kB)

Abstract

The present research establishes a relationship of bulged diameter with densification and hydrostatic stress in forming of sintered iron (Fe) powder metallurgy preforms cold upset under two different frictional conditions, namely, nil/no and graphite lubricant condition. Sintered plain carbon steel cylindrical preforms with carbon (C) contents of 0, 0.35, 0.75 and 1.1% with constant initial theoretical density of 84% and aspect ratio of 0.4 and 0.6 were prepared using a suitable die-set assembly on a 1 MN capacity hydraulic press and sintered for 90 minutes at 1200 °C. Each sintered preform was cold upset under two different frictional constraints. It is seen that the degree of bulging reduces with reducing frictional constraints at the die contact surface. Further, it is found that the bulging ratio changed as a function of relative density and hydrostatic stress, respectively, according to the power law equations.

Item Type:	Journal Article
Subjects:	T Technology > TJ Mechanical engineering and machinery
Divisions:	Faculty of Science, Technology and Environment (FSTE) > School of Engineering and Physics
Depositing User:	Ms Shalni Sanjana
Date Deposited:	23 Jan 2013 22:22
Last Modified:	08 Jan 2017 21:38
URI:	http://repository.usp.ac.fj/id/eprint/5410

UNSPECIFIED

Actions (login required)

View Item